Transcript
CL200
2V 200Ah(10hr)
The rechargeable batteries are lead-lead dioxide systems. The dilute sulfuric acid electrolyte is absorbed by separators and plates and thus immobilized. Should the battery be accidentally overcharged producing hydrogen and oxygen, special one-way valves allow the gases to escape thus avoiding excessive pressure build-up. Otherwise, the battery is completely sealed and is, therefore, maintenance-free, leak proof and usable in any position. Battery Construction Component
Positive plate
Negative plate
Container
Cover
Safety valve
Terminal
Separator
Electrolyte
Raw material
Lead dioxide
Lead
ABS
ABS
Rubber
Copper
Fiberglass
Sulfuric acid
General Features ●
●
● ● ●
●
● ●
Performance Characteristics
Absorbent Glass Mat (AGM) technology for efficient gas recombination of up to 99% and freedom from electrolyte maintenance or water adding. Not restricted for air transport-complies with IATA/ICAO Special Provision A67. UL-recognized component. Can be mounted in any orientation. Computer designed lead, calcium tin alloy grid for high power density. Long service life, float or cyclic applications. Maintenance-free operation. Low self discharge.
Dimensions and Weight Length(mm / inch) Width(mm / inch) Height(mm / inch) Total Height(mm / inch) Approx. Weight(Kg / lbs)
173 / 6.81 111 / 4.37 329 / 12.96 341 / 13.42 15 / 33.1
Nominal Voltage 2V Number of cell 1 Design Life 20 years Nominal Capacity 77oF(25oC) 10 hour rate (20A, 1.8V) 200Ah 5 hour rate (36.3A, 1.75V) 181.5Ah 1 hour rate (124A, 1.6V) 124Ah Internal Resistance 0.67mOhms Fully Charged battery 77oF(25oC) Self-Discharge 3% of capacity declined per month at 20oC(average) Operating Temperature Range Discharge -20~60oC Charge -10~60oC Storage -20~60oC o o 1000A(5s) Max. Discharge Current 77 F(25 C) Charge Methods: Constant Voltage Charge 77oF(25oC) Cycle use 2.35-2.45V Maximum charging current 40A Temperature compensation -5.0mV/oC Standby use 2.25-2.3V Temperature compensation -3.3mV/oC
Discharge Constant Current (Amperes at 77oF25oC) End Point Volts/Cell 1.60V 1.65V 1.70V 1.75V 1.80V
10min 15min 30min 45min 392 372 350 329 307
294 280 265 250 235
196 187 178 169 160
162 155 148 141 134
1h
3h
5h
10h
124 120 115 110 104
56.6 54.8 52.9 50.8 48.6
39.3 38.4 37.4 36.3 35.0
21.4 21.2 20.9 20.5 20.0
Discharge Constant Power (Watts at 77oF25oC) End Point Volts/Cell 1.60V 1.65V 1.70V 1.75V 1.80V
10min 15min 30min 45min 580 559 538 517 495
524 499 473 446 420
380 364 348 331 315
308 299 289 280 272
1h
2h
3h
5h
245 235 224 213 201
146 142 137 132 126
106 104 101 98.0 94.7
78.0 76.6 75.1 73.5 71.7
(Note)The above characteristics data are average values obtained within three charge/discharge cycles not the mimimum values.
page1 of 2
www.vision-batt.com
+
-
Current
Charged Volume
O
Discharge characteristic (25 C)
Voltage
CL200
(%) (xCA)
Voltage(V)
2.0
2V200Ah
Charge characteristic curve Constant voltage charge characteristic o (0.2CA,25 C)
(V)
140
50.8A 36.3A
20A
120
0.25
100
0.20
80
1.6
400A
200A
124A
1
2
3
5
20 30
10 min
CHARGE VOLTAGE 2.25
0.15
60 0.10
40 0
CHARGED VOLUME
2.50
60
2
3
5
10
20
20
0.05
0
0
h
2.00
CHARGING CURRENT 1.75
0
Discharge time
2
4
6
8
10
12
14
16
18
20
Charging time (hours)
Relationship between charging voltage and temperature
Self-discharge characteristic 110 100
2.6 Capacity(%)
Voltage (V)
90 2.5
CYC
2.4
LE U
S TA N
2.3
SE
D BY
80 70 60
USE
2.2
-10
0
10 20 30 o Ambient temperature( C)
40
40
50
0
2
6
8 10 12 14 Storage time: months
80 60 Testing conditions: floating voltage: 2.25 to 2.30V/Cell o o ambient temperature: 25 C(77 F)
18
20
80 60
40
40
20
20
0
5
10 Life(year)
100% D.O.D.
0
15
400
50% D.O.D.
800
1200
30% Depth of discharge
1600
2000
2400
Number of cycles(cycles)
Temperature effects on float life
Temperature effects on capacity 120
25
100
2.30V/Cell
0.1C
Capacity (%)
20 Life(years)
16
100 Capacity(%)
Capacity(%)
4
120
100
10
5
0.2C 0 .3 C
80 60
1 .0 C
40
2 .0 C
20 0
20 oC
Cycle service life in relation to depth of discharge
Life characteristics of standby use 120
0
30 oC
40 oC
50
10
20
30
40
0
50
-20
-10
Temperature( oC)
THE INTERNATIONAL CERTIFICATION NETWORK
ISO9001:2000
MH25860
0
10 20 Temperature( oC)
30
40
G4M19906-9202-E-16
www.vision-batt.com
Shenzhen Center Power Tech. Co., Ltd. Center Power Industrial Park, Tongfu Industrial District Dapeng Town, 518120 Shenzhen, China Tel: (+86-755) 8431 8088 Fax: (+86-755) 8431 8038 E-mail:
[email protected] Copy Right Shenzhen Center Power Technology Co., Ltd (Edition 2003-9)
Page 2 of 2
50